用途：
用于制作强酸强碱化工行业耐腐蚀电极以及其他耐腐蚀零件；用于制作高温真空炉中耐高温紧固件及其他耐高温零件；在航空航天、医疗植入以及半导体电子等领域均有广泛应用。
Applications:
They
are used to make corrosion-resistant electrodes and other
corrosion-resistant parts in the strong acid and alkali chemical
industry, and high-temperature resistant fasteners and other
high-temperature parts in the high-temperature vacuum furnace; they are
widely used in the fields of aerospace, medical implant and
semiconductor electronics, etc.
产品性能参数/Product Property Parameters：
|
牌号
Grade
|
Ta1
|
TaW2.5
|
TaW10
|
|
主含量，
Main Content, %,
|
Ta
|
99.95,min
|
余量
Balance
|
余量
Balance
|
|
化学成分Chemical Compositions（%，不大于/max）
|
C
|
0.01
|
0.01
|
0.01
|
|
N
|
0.005
|
0.01
|
0.01
|
|
H
|
0.0015
|
0.0015
|
0.0015
|
|
O
|
0.015
|
0.015
|
0.015
|
|
Nb
|
0.02
|
0.05
|
0.05
|
|
Fe
|
0.005
|
0.01
|
0.01
|
|
Ti
|
0.002
|
0.01
|
0.01
|
|
W
|
0.005
|
2.0-3.5
|
9.0-11.0
|
|
Mo
|
0.005
|
0.02
|
0.02
|
|
Si
|
0.005
|
0.005
|
0.005
|
|
Ni
|
0.002
|
0.01
|
0.01
|
|
机械性能
（退火态）
Mechanical Properties（Annealing）
|
抗拉强度
Tensile Strength
（MPa，不小于/min）
|
172
|
276
|
482
|
|
屈服强度
Yield strength
（MPa，不小于/min）
|
103
|
193
|
379
|
|
伸长率
Elongation
（％，不小于/min）
|
25
|
20
|
20
|
尺寸Size & 公差 Tolerance: （毫米/mm，不大于/max）
|
直径
Diameter (mm)
|
直径公差
Diameter Tolerance (mm)
|
长度
Length (mm)
|
长度
Length (mm)
|
|
2.0-4.0
|
±0.05
|
500-3000
|
±2
|
|
＞4.0-8.0
|
±0.06
|
50-3000
|
±2
|
|
＞8.0-12.0
|
±0.08
|
50-3000
|
±2
|
|
＞12.0-20.0
|
±0.10
|
50-2000
|
±2
|
|
＞20.0-36.0
|
±0.15
|
50-2000
|
±2
|
|
＞36.0
|
±0.20
|
50-2000
|
±2
|
如有特殊要求，双方具体商定。
Note: Special requirements will be agreed upon by the supplier and buyer.